Active Thermitic Material Discovered in Dust from the 9/11 World Trade Center Catastrophe

Global Research, April 3, 2009

Below is the Abstract, Introduction and Conclusions of this important and carefully researched article

The complete article can be downloaded (pdf)

Active Thermitic Material Discovered in Dust from the 9/11 World Trade Center Catastrophe

pp.7-31 (25)

Authors: Niels H. Harrit, Jeffrey Farrer, Steven E. Jones, Kevin R. Ryan, Frank M. Legge, Daniel Farnsworth, Gregg Roberts, James R. Gourley, Bradley R. Larsen

The Open Chemical Physics Journal

Volume 2

ISSN: 1874-4125

doi: 10.2174/1874412500902010007

Complete Article

http://www.bentham-open.org/pages/content.php?TOCPJ/2009/00000002/00000001/7TOCPJ.SGM


Abstract:

We have discovered distinctive red/gray chips in all the samples we have studied of the dust produced by the destruction of the World Trade Center. Examination of four of these samples, collected from separate sites, is reported in this paper. These red/gray chips show marked similarities in all four samples. One sample was collected by a Manhattan resident about ten minutes after the collapse of the second WTC Tower, two the next day, and a fourth about a week later. The properties of these chips were analyzed using optical microscopy, scanning electron microscopy (SEM), X-ray energy dispersive spectroscopy (XEDS), and differential scanning calorimetry (DSC). The red material contains grains approximately 100 nm across which are largely iron oxide, while aluminum is contained in tiny plate-like structures. Separation of components using methyl ethyl ketone demonstrated that elemental aluminum is present. The iron oxide and aluminum are intimately mixed in the red material. When ignited in a DSC device the chips exhibit large but narrow exotherms occurring at approximately 430 ?C, far below the normal ignition temperature for conventional thermite. Numerous iron-rich spheres are clearly observed in the residue following the ignition of these peculiar red/gray chips. The red portion of these chips is found to be an unreacted thermitic material and highly energetic.

http://www.globalresearch.ca/index.php?context=va&aid=13049

Commence braying, asses!

 

[Nelson]

CONCLUSIONS

We have discovered distinctive red/gray chips in significant numbers in dust associated with the World Trade Center destruction. We have applied SEM/XEDS and other methods to characterize the small-scale structure and chemical signature of these chips, especially of their red component. The red material is most interesting and has the following characteristics:

1. It is composed of aluminum, iron, oxygen, silicon and carbon. Lesser amounts of other potentially reactive elements are sometimes present, such as potassium, sulfur, lead, barium and copper.

2. The primary elements (Al, Fe, O, Si, C) are typically all present in particles at the scale of tens to hundreds of nanometers, and detailed XEDS mapping shows intimate mixing.

3. On treatment with methyl ethyl ketone solvent, some segregation of components occurred. Elemental aluminum became sufficiently concentrated to be clearly identified in the pre-ignition material.

4. Iron oxide appears in faceted grains roughly 100 nm across whereas the aluminum appears in thin platelike structures. The small size of the iron oxide particles qualifies the material to be characterized as nanothermite or super-thermite.

5. Analysis shows that iron and oxygen are present in a ratio consistent with Fe2O3. The red material in all four WTC dust samples was similar in this way. Iron oxide was found in the pre-ignition material whereas elemental iron was not.

6. From the presence of elemental aluminum and iron oxide in the red material, we conclude that it contains the ingredients of thermite.

7. As measured using DSC, the material ignites and reacts vigorously at a temperature of approximately 430 ?C, with a rather narrow exotherm, matching fairly closely an independent observation on a known super-thermite sample. The low temperature of ignition and the presence of iron oxide grains less than 120 nm show that the material is not conventional thermite (which ignites at temperatures above 900 ?C) but very likely a form of super-thermite.

8. After igniting several red/gray chips in a DSC run to 700 ?C, we found numerous iron-rich spheres and spheroids in the residue, indicating that a very high temperature reaction had occurred, since the iron-rich product clearly must have been molten to form these shapes. In several spheres, elemental iron was verified since the iron content significantly exceeded the oxygen content. We conclude that a high-temperature reduction-oxidation reaction has occurred in the heated chips, namely, the thermite reaction.

9. The spheroids produced by the DSC tests and by the flame test have an XEDS signature (Al, Fe, O, Si, C) which is depleted in carbon and aluminum relative to the original red material. This chemical signature strikingly matches the chemical signature of the spheroids produced by igniting commercial thermite, and also matches the signatures of many of the microspheres found in the WTC dust [5].

10. The carbon content of the red material indicates that an organic substance is present. This would be expected for super-thermite formulations in order to produce high gas pressures upon ignition and thus make them explosive. The nature of the organic material in these chips merits further exploration. We note that it is likely also an energetic material, in that the total energy release sometimes observed in DSC tests exceeds the theoretical maximum energy of the classic thermite reaction.

Based on these observations, we conclude that the red layer of the red/gray chips we have discovered in the WTC dust is active, unreacted thermitic material, incorporating nanotechnology, and is a highly energetic pyrotechnic or explosive material.

 

[smurphy]

he's like a pt1gard alter-ego that wants to kill jews and blacks

 

[RAYMOND]

he's like a pt1gard alter-ego that wants to kill jews and blacks

left out fags

 

[Nelson]

he's like a pt1gard alter-ego that wants to kill jews and blacks

Pure T.

 

[I LOVE WR]

what is this guy talking about?? The USgov't is nothing but honest hard working Americans trying to make the country better for all. what a douche

 

[Nelson]

what is this guy talking about?? The USgov't is nothing but honest hard working Americans trying to make the country better for all. what a douche

I wish we could bet on who's responsible for WTC takedown.

Of course there's been a long thread on this here, and I don't wish to reopen as people are for the most part set in their opinions. But as new information comes up, it's worth taking note of.